i agree... this is a machine that needs some experimenting to take the best of of it.. i choose to work on leaded solder cause lead free is general known as a beast...of course it will add more trouble on the solder quality. i think it needs a large casistic to evaluate the results on the long run. If you repair several boards at week, long therm failing (but not too long) can be very painful for your pocket.
on the last, a general methode can't be wrote down, cause even changing the board form factor will add new rules in the game.
i'm looking for a solution to give to this baby a real thermal control. i will see |